Typical Properties | Compatible Substrates | |||||||||
% Solids | Viscosity (Cp @25°C) |
Application | Cure | Typical FT(μm) |
Typical Bayer |
PC | PMMA | PET | HIRI | PA |
30 - 34 | 3.0 - 7.0 | Dip/spin | 800-900mJ/cm2 | 3.0 - 5.0 | 1.5 | ✔ | ✔ | ∎ | ∎ | |
30 -34 | 4.0 - 7.0 | Dip/spin | 900mJ/cm2 | 3.5 - 5.0 | ≥1.5 | ✔ | ✔ | ✘ | ∎ | |
6.0 - 8.0 | ∎ | ∎ | ∎ | ∎ | ∎ | |||||
38 -42 | 6.0 - 10.0 | Spray | 1-2 J/cm2 PMMA 2-3 J/cm2 |
8 - 10 PMMA 13 - 15 |
- | ✔ | ✔ | ✘ | ∎ | ✘ |
65 - 70 | 12.0 - 17.0 | Dip/spin/ roll to roll |
800-900mJ/cm2 | 5.0 - 10.0 | ≥1.3 | ✔ | ∎ | ✔ | ∎ | ∎ |
34.5 - 36.5 | 9.0 - 11.0 | Spin | 0.9-1.0 J/cm2 1hr @ |
3.0 - 5.0 | 2.0 - 4.0 | ✔ | ∎ | ∎ | ∎ | ∎ |
34.5 - 36.5 | 9.0 - 11.0 | Spin | 0.9-1.0 J/cm2 1hr @ |
3.0 - 5.0 | 2.0 - 4.0 | ✔ | ∎ | ∎ | ∎ | ∎ |
100 | 35 - 100 | Spin | 1.1-1.20 J/cm2 | 6.0 - 9.0 | ≈2 | ✔ | ∎ | ∎ | ∎ | ✔ |
100 | 35 - 45 | Spin | 1.1-1.20 J/cm2 | 5.0 - 7.0 | 1.5 | ✔ | ∎ | ∎ | ✔ | ∎ |
30 -34 | ≤10 | Dip | 1.2 J/cm2 PC 2.0 J/cm2 PA |
3.5 - 4.0 | ≈2 | ✔ | ✔ | |||
46 - 52 | 8.0 - 15.0 | Dip | 1.6 J/cm2 PC 30 mins @100℃ |
5.0 - 7.0 | 1.5 - 2.5 | ✔ | ||||
100 | 35 - 40 | Spin | 2.2 J/cm2 | 4.0 - 6.0 | 1.7 | ✔ | ✔ | ✔ | ✔ | |
23 | 1.0 - 1.5 | Spin | 2.0 J/cm2 | 1.2 - 1.5 | 1.8 | ∎ | ||||
45 | 17.5 - 18.5 | Di✔ | 2.0 J/cm2 | 4.5 - 5.0 | 1.8 | ✔ | ✔ | |||
52 | 10 - 14 | Dip | 1.50 J/cm2 | 4.0 - 5.0 | 1.1 | ✔ | ✔ | |||
100 | 35 - 40 | Spry, Spin | 2.0 J/cm2 | 10 - 25 | ✔ | ✔ | ✔ | |||
46 | 7.5 - 8.5 | Spin | 2.0 J/cm2 | 4.0 - 5.0 | 1.5 | ✔ |